Gate Conductor Structure

ABSTRACT

A gate conductor structure is provided having a barrier region between a N-type device and a P-type device, wherein the barrier region minimizes or eliminates cross-diffusion of dopant species across the barrier region. The barrier region comprises at least one sublithographic gap in the gate conductor structure. The sublithographic gap is formed by using self-assembling copolymers to form a sublithographic patterned mask over the gate conductor structure. According to one embodiment, at least one sublithographic gap is a slit or line that traverses the width of the gate conductor structure. The sublithographic gap is sufficiently deep to minimize or prevent cross-diffusion of the implanted dopant from the upper portion of the gate conductor. According to another embodiment, the sublithographic gaps are of sufficient density that cross-diffusion of dopants is reduced or eliminated during an activation anneal such that changes in Vt are minimized.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a divisional of currently co-pending U.S. patentapplication Ser. No. 11/609,496, filed on Dec. 12, 2006, the subjectmatter of which is incorporated herein by reference in its entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to semiconductor devices of different types thatclosely spaced and are connected by conductive connectors. Morespecifically, the present invention relates to different complementarymetal-oxide-semiconductor (CMOS) devices that are adjacent to eachother, such as n-channel field effect transistors (n-FETs) and p-channelfield effect transistors (p-FETs), which connected by conductiveconnectors that include different dopants associated with the differentCMOS devices.

2. Description of Related Art

As semiconductor devices scale, spacing between the CMOS devices becomesmaller. Devices of different types, such as field effect transistors(FETs) having different performance characteristics, may be placedadjacent to each other, and share certain physical components. Forexample, in devices such as a static random access memory (SRAM),adjacent pFET and nFET devices may share a common gate conductor, whichat the pFET includes a different dopant than at the nFET.

However, as the spacing between devices decreases, dopants of differenttypes may diffuse along a shared gate conductor to such an extent thatit encroaches on and changes the properties of the adjacent devicehaving a different dopant. Such cross diffusion may adversely alterproperties such as the threshold voltage of a transistor. The undesiredvariation of device property results in poor product performance andyield.

For example, FIG. 1 illustrates an nFET device 20 adjacent to a pFETdevice 30, having channel regions 21, 31 formed in a semiconductorsubstrate 4. The nFET 20 is electrically isolated from the pFET 30 byisolation regions 25. Gate dielectric layers 24 are formed atop thechannel region of the nFET 21 and the channel region of the pFET 31.Overlaying both the nFET channel 21 and pFET channel 31 atop the gatedielectric 24 is a gate conductor 10, which includes an N+ doped region10′ over the nFET channel 21 and a P+ doped region 10″ over the pFETchannel 31. A spacer 12 is formed on the sidewalls of the gate conductor10. However, the N+ and P+ dopants may cross diffuse in the gateconductor region 10″′ between the nFET and pFET due to effects such asimplant mask overlay errors and thermal anneal. If the cross-diffusionregion 10″′ encroaches over the channel regions of the nFET or pFEt,there may be changes in work function. To avoid this problem, thespacing 14 between the nFET and pFET must be maintained sufficientlylarge so that the cross-diffusion region 10″′ encroachment over thedevice channel will be minimized, which limits scaling of chip density.

Referring to FIG. 2, the Vt for a pFET, which is adjacent an nFET in anSRAM, is plotted on the vertical axis as a function of gate length Lpolybetween the pFET and the nFET. The lower grouping of data points (line33) represents widely spaced devices. The dark filled circles representdata points without additional thermal anneal while the filled trianglesrepresent data points with additional thermal budget. Since the nFET andpFET are sufficiently spaced apart, there would be no Vt shift. However,if the nFET and pFET are sufficiently close together (open circles 35and triangles 37), the additional thermal budget (open triangles 37)exhibit a significant shift in Vt due to cross diffusion relative to thepFETs prior to the anneal (open circles 35).

In view of the above, it would be desirable to form a gate conductorstructure with reduced dopant cross diffusion without impacting densityof the circuit layout and allow scaling of closely spaced devices.

SUMMARY OF THE INVENTION

The present invention provides a method that combines a conventionallithographic technology with the self-assembling block copolymertechnology to achieve a sub-lithographic dimension slit in a gateconductor to reduce dopant diffusion in CMOS devices.

Dopant diffusion is determined by the cross-sectional area of thediffusion path. As the diffusion path area is reduced, diffusion isreduced. It is desirable to create a slit or an air gap in the diffusionpath with sublithographic dimension hence not to impact circuit layoutdensity.

Self-assembling block copolymers are capable of self-organizing intonanometer-scale patterns, enabling future advances in the semiconductortechnology. Each self-assembling block copolymer system typicallycontains two or more different polymeric block components that areimmiscible with one another. Under suitable conditions, the two or moreimmiscible polymeric block components separate into two or moredifferent phases on a nanometer scale and thereby form ordered patternsof isolated nano-sized structural units.

According to a first aspect of the invention, a gate conductor structureis provided comprising a sublithographic gap having a sublithographicdimension. The sublithographic gap preferably traverses the width of thegate conductor structure. The sublithographic gap is preferably locatedbetween a N-type and a P-type device. The gap preferably extends from atleast the upper portion of said gate conductor structure where animplant concentration is highest.

According to another aspect of the invention, a gate conductor structurecomprises a barrier region between a N-type and a P-type device.According to a first embodiment, the barrier region comprises asublithographic gap that traverses the width of the gate conductorstructure. According to another embodiment, the sublithographic gapextends to a depth so that the concentration of said dopant at thebottom of the gap is less than 50% of the highest concentration of saiddopant in the gate conductor.

According to another aspect of the invention, the barrier regioncomprises a plurality of sublithographic features having a sufficientlyhigh density such that the step of patterning said gate conductor formsa barrier region such that diffusion of dopants across the barrierregion is reduced or eliminated during an activation anneal so thatchanges in Vt are minimized.

These and other aspects of the embodiments of the invention will bebetter appreciated and understood when considered in conjunction withthe following description and the accompanying drawings. It should beunderstood, however, that the following descriptions, while indicatingpreferred embodiments of the invention and numerous specific detailsthereof, are given by way of illustration and not of limitation. Manychanges and modifications may be made within the scope of theembodiments of the invention without departing from the spirit thereof,and the embodiments of the invention include all such modifications.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be understood and appreciated more fully fromthe following detailed description of the invention, taken inconjunction with accompanying drawings of which:

FIGS. 1A-1C illustrates top-down and cross-sectional views of prior artadjacent nFET and pFET structures that share a gate conductor having across-diffusion region.

FIG. 2 illustrates Vt shift in a pFET device due to cross-diffusion in agate conductor.

FIGS. 3A-3C illustrates a cross-sectional view of simulations of dopantconcentration in a gate conductor.

FIGS. 4A-4C illustrates top-down and cross-sectional views of oneembodiment of a gate conductor structure according to the invention.

FIGS. 5A-5C illustrates top-down and cross-sectional views of oneembodiment of a gate conductor structure according to the invention.

FIGS. 6A-6C illustrates top-down and cross-sectional views at anintermediate step for forming a gate conductor structure according to anembodiment of the invention.

FIGS. 7A-7B through 9A-9B and 11A-11B through 14A-14B illustratetop-down and a cross-sectional view of the structure during processsteps of an embodiment of a method of forming the inventive structure.

FIG. 10A illustrates a top-down view of an SEM of a diblock copolymerhaving a self-organized pattern substantially co-linear with a hardmaskopening.

FIG. 10B illustrates a schematic cross-sectional view of the diblockcopolymer linear pattern of FIG. 10A.

FIGS. 15A-15C illustrates top-down and cross-sectional views of a gateconductor structure according to an embodiment of the present invention.

It will be appreciated that for simplicity and clarity of illustration,elements shown in the drawings have not necessarily been drawn to scale.For example, the dimensions of some of the elements may be exaggeratedrelative to other elements for purposes of clarity.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides for a method that combines a conventionallithographic process with self-assembling block copolymer technology toachieve a structure including a sub-lithographic barrier region in agate conductor structure that reduces dopant diffusion in CMOS devices.

Self-assembling block copolymers are capable of self-organizing intonanometer-scale patterns. See, for example, C. T. Black, “Integration ofSelf Assembly for Semiconductor Microelectronics”, Proceedings IEEE 2005Customer Integrated Circuits Conference, pp. 87-91, the disclosure ofwhich is hereby incorporated by reference in its entirety. Eachself-assembling block copolymer system typically contains two or moredifferent polymeric block components that are immiscible with oneanother. Under suitable conditions, the two or more immiscible polymericblock components separate into two or more different phases on ananometer scale and thereby form ordered patterns of isolated nano-sizedstructural units.

Dopant diffusion is determined by the cross-sectional area of thediffusion path. As the cross-sectional area of the diffusion path areais reduced, diffusion is reduced. Thus, it would be desirable to reducethe cross-sectional area of the diffusion path in the gate conductorwithout impacting circuit layout density.

In accordance with the present invention, a sub-lithographic openings orair gaps are formed in the gate conductor between adjacent devices toform a barrier region such that the cross-sectional area of thediffusion path is significantly reduced or eliminated. In accordancewith the invention, the sub-lithographic openings in the barrier regionare formed using a self-assembling copolymer process to form the barrierregion.

Referring to FIG. 3, a simulation of phosphorus concentration in ann-doped gate conductor is illustrated. FIG. 3A illustrates theconcentration of the phosphorus as implanted. Note that the region ofhighest concentration 39 is near the surface of the gate conductor afterimplantation. FIG. 3B illustrates diffusion after a first anneal butbefore a second anneal. FIG. 3C illustrates the concentration after asecond anneal, designated as REOX anneal. Note that even after the firstanneal and REOX anneal, the highest concentration of phosphorous is nearthe top of the gate conductor.

Referring to FIGS. 4A-4C, according to one embodiment of the presentinvention, slits or airgaps are provided in a barrier region 150 withinthe gate conductor 110 between the nFET 120 and the pFET 130. A spacer12 is formed on the sidewalls of the gate conductor 110. The gateconductor 110 includes a first doped region 110′ and a second dopedregion 110″ positioned over the nFET channel 121 and pFET channel 131,respectively. The barrier region 150 is located between the first dopedregion 110′ and the second doped region 110″. Preferably slits orairgaps in the barrier region 150 traverse the width of the gateconductor 110 so as to substantially reduce or eliminate thecross-sectional area of the diffusion path between the nFET 120 and thepFET 130. The depth of the gaps need not extend all the way to thebottom of the gate conductor 110, since the highest concentration ofdopant is likely to be near the top of the gate conductor 110 where thedopant was implanted. Preferably the depth of the gap is such that theconcentration of the dopant at the bottom of the air gap is less than50% of the highest dopant concentration in the gate conductor.

Subsequently, referring to FIG. 5, a silicide may be formed on top ofthe gate conductor 110 and the source/drain regions, including over thegaps in the barrier region 150. The silicide, or semiconductor-metalalloy, is formed by sputtering metal on the surface of the wafer. Duringa subsequent anneal step, metal reacts with silicon including siliconsubstrate (source and drain) and silicon in the gate conductor. Thenon-reacted metal is then stripped from the wafer surface. This processis commonly called salicidation. The metal silicide may be formed on thetop, sidewalls, and bottom of the air gaps.

FIGS. 6-9 and 11-15 illustrate process steps, according to oneembodiment of the invention, for forming a diffusion barrier region 150.FIG. 6 illustrates a semiconductor structure including nFET 120 and pFET130 regions formed in the semiconductor substrate 4, which may be formedby methods now known in the art, or developed in the future. Isolationregions 125 are between the nFET 120 and pFET 130 regions. The gateconductor 110 is formed atop gate dielectrics 24 over the nFET channel121 and pFET channel 131. Spacers 12 may be formed on the sidewalls ofthe gate conductor 110. The gate conductor 110 includes a first dopedregion 110′, e.g. N+ dopants in the nFET region 120, and a second dopedregion 110″, e.g. P+ dopants in the pFET region 130. In addition,implants are formed in the substrate 4 adjacent the gate conductors toform source/drain regions (not shown) for the nFET and pFET, as is knownin the art. Commonly used N+ dopants include As, P, and Sb, and P+dopants include B and In. A sacrificial dielectric layer 125, such as aspin-on low k dielectric, is deposited over the structure, and thenplanarized to be coplanar with the gate conductor 110, for example, bychemical-mechanical polishing (CMP).

Next, referring to FIG. 7, a hardmask 145 is formed over the structureof FIG. 6, and patterned to form an opening 75 that exposes the gateconductor between the first doped region 110′ and the second dopedregion 110″ in the gate conductor. For example, this may be done bydepositing a hardmask layer, comprising, for example, SiN or SiC, atopthe planarized surface of the gate conductor 110, the spacers 12 andsacrificial 125. The hardmask may be patterned by any suitable methodknown in the art, for example, by depositing a photoresist layer,patterning an opening in the photoresist layer using a lithographicprocess (not shown) and transferring the patterned opening into thehardmask using an anisotropic etch, such as reactive ion etch (RIE). Theresist layer is then removed, resulting in the structure illustrated inFIG. 7.

Next, referring to FIG. 8, a diblock copolymer 152 is applied atop thestructure of FIG. 7, so that the opening 75 is filled. A diblockcopolymer consists of two immiscible polymer blocks that covalently bondat one end of each other. When given sufficient mobility, theyself-assemble to minimize surface energy. Preferably, first and secondpolymeric block components have a weight ratio of from about 80:20 toabout 60:40. According to a preferred embodiment, the diblock copolymercomprises polystyrene (PS) and poly (methyl-methacrylate) (PMMA), withPS-b-PMMA having a PS:PMMA weight ratio ranging from about 80:20 toabout 60:40. The thickness of the diblock film can be controlled by spinspeed and concentration of a solvent, for example, toluene. The surfaceof the wafer is preferably be treated with a neutralizing layer 69 (seeFIG. 10), which is a random copolymer that is composed of monomers fromthe two copolymer blocks.

Next, referring to FIG. 9, an anneal is performed to form regularpatterns in the diblock copolymer 152 within the filled opening 75.Preferably the regular patterns comprise patterns 92 that are organizedin elongated, preferably linear, patterns that traverse the width of thegate conductor 110. Formation of linear patterns may be controlled byadjusting the ratio of copolymers and by adjusting the wettingproperties of the neutralization layer 69 relative to one of the diblockcopolymers. Such dimensions of the self-organized patterns aresublithographic due to the molecular weight and dimension of theself-organizing copolymer molecules. In other words, the width of thepatterns will be typically approximately equal to a small multiple ofthe length of the copolymer molecules. Note that the copolymer depositedoutside the opening 75 will not typically be too thin to form organizedpatterns. Even if such patterns do form, they will not be transferred tothe underlying substrate except through the opening 75.

For example, FIG. 10A illustrates a top-down view of a scanning electronmicroscope (SEM) image of a linear hardmask opening filled with anasymmetric diblock copolymer composed of 70% polystyrene (PS) and 30%poly(methyl-methacrylate) (PMMA) after annealing at 180° C. FIG. 10B isa schematic cross-section along the line C-C in FIG. 10A. The PMMA hasself-organized into lines 72 that run substantially parallel to thelengthwise orientation of the hardmask opening 87. A surfaceneutralization layer 69 is located between the diblock copolymer and thesubstrate. The surface neutralization layer 69 comprises a randomcopolymer monomer.

Next, referring to FIG. 11, the copolymer that forms the regularpatterns is removed, for example, by immersing the copolymer system inan acetic acid solution to form openings 98 in the annealed copolymerlayer 152. Preferably, the width of the openings 98 are in the rangefrom about 5 nm to about 40 nm, and most preferably from about 10 nm to30 nm.

Next, referring to FIG. 12, the patterned copolymer layer 152 is used asa mask, and an anisotropic etch is performed, e.g. by a RIE process, totransfer the openings 98 into the gate conductor 110 to form the barrierregion 150. The openings 98 may extend through the gate conductor 110and terminate on the STI 25 so as to form a physical barrier todiffusion. Optionally, the openings 98 may terminate at a depth withinthe gate conductor that is sufficiently deep so that diffusion isminimized, and the highest concentration of dopants in an upper portionof the implanted gate conductor is substantially prevented fromcross-diffusion across the barrier region 150. Alternatively, theopenings 98 need not be limited to elongated patterns that traverse thewidth of the gate conductor, but may be organized into a sufficientlyhigh density of patterned openings so that cross-diffusion across thebarrier region 150 is minimized. Such high density patterns may beformed by altering the copolymer composition or surface neutralizationlayer property. The high density sublithographic patterns are preferablyconfigured so as to reduce cross-diffusion of an implant species acrossthe barrier region to a minimal amount during an activation anneal, suchthat changes in Vt are minimized.

Next, the copolymer layer 152 and the hardmask 145 are removed,resulting in the structure illustrated in FIG. 13.

Next, the sacrificial layer 125 is removed, resulting in the structureillustrated in FIG. 14.

Next, a dopant activation anneal is applied to activate the implanted N+dopants 110′ and P+ dopants 110″, for example, at a temperature betweenabout 900 to 1100° C. At these temperatures, diffusion of the dopantswill occur. In accordance with the invention, the density and/or extentof the gaps in the barrier region will minimize or preventcross-diffusion between the N+ and P+ regions during such an activationanneal, so that the changes in Vt are minimized, to an amount accordingthe requirements of a particular circuit application.

Subsequently, a silicide or semiconductor-metal alloy 160 may be formedatop the semiconductor substrate over the source/drain regions adjacentthe gate conductor and the gate conductor 110, including within the airgaps (not shown). Then, the devices may be completed, as known in theart.

The inventive barrier region 150 has the advantage of completely orsubstantially preventing cross-diffusion between adjacent devices thathave different dopant species, thus avoiding cross-diffusion withoutimpacting layout density as the ground rules shrink.

While certain features of the invention have been illustrated anddescribed herein, many modifications, substitutions, changes, andequivalents will now occur to those of ordinary skill in the art. It is,therefore, to be understood that the appended claims are intended tocover all such modifications and changes as fall within the spirit ofthe invention.

1. A semiconductor structure comprising: a gate conductor structurecomprising a sublithographic gap having a sublithographic dimension. 2.The semiconductor conductor structure in claim 1 wherein saidsublithographic gap traverses a width of said gate conductor structure.3. The semiconductor conductor structure in claim 1 wherein saidsublithographic gap is located between a N-type and a P-type device. 4.The semiconductor conductor structure of claim 2 wherein saidsublithographic gap extends from at least the upper portion of said gateconductor structure.
 5. The semiconductor conductor structure in claim 3wherein said sublithographic gap extends from at least the upper portionof said gate conductor structure where the concentration of a dopant ishighest.
 6. The semiconductor conductor structure in claim 5 whereinsaid sublithographic gap extends to a depth so that a concentration ofsaid dopant at the bottom of the gap is less than 50% of the highestconcentration of said dopant in the gate conductor.
 7. The semiconductorconductor structure comprising: a gate conductor structure comprising abarrier region between a N-type and a P-type device.
 8. Thesemiconductor structure in claim 7 wherein said barrier region comprisesa sublithographic gap having a sublithographic dimension.
 9. Thesemiconductor structure in claim 7 wherein said barrier region comprisesa plurality of sublithographic gaps wherein said gaps have asublithographic dimension, and wherein said plurality of sublithographicgaps are configured so as to reduce cross-diffusion of an implantspecies across said barrier region during an activation anneal so thatchanges in Vt are minimized.
 10. The semiconductor structure in claim 8wherein said sublithographic gap traverses a width of said gateconductor structure.
 11. The semiconductor structure in claim 10 whereinsaid sublithographic gap extends from at least the upper portion of saidgate conductor structure.
 12. The semiconductor conductor structure inclaim 7 wherein said sublithographic gap extends from at least the upperportion of said gate conductor structure where a concentration of adopant is highest.
 13. The semiconductor conductor structure in claim 12wherein said sublithographic gap extends to a depth so that theconcentration of said dopant at the bottom of the gap is less than 50%of the highest concentration of said dopant in the gate conductor.